Top welding guides: how to become a better welder and how to select the top welding equipment. For DCEN welding on steels, 1/16″ will work in the 20 to 100 amp rage as long as you prep it right. If you are using 20 amps, you will need a needle sharp point to get good crisp arc starts. At 100 amps, you might not want quite a needle sharp point or you might be putting a smidge of tungsten in the weld. You need a blunter taper. Some charts extend the range to 150 amps for 1/16, but I think that’s way too much. Why not just swap to a 3/32 at that amperage.? 3/32″ is good from about 65 – 200 amps. And 1/8″ 2% thoriated electrodes are good in the 85 – 300 amp range. ( Drop all these numbers by about 30% for A/C) Using helium mixed with the argon will also change the recommended currents because the arc is hotter with the same amps. These recommendations are from down and dirty experience and don’t come from a chart. Most charts I have seen tell you a 1/16 tungsten is good all the way to 150 amps…Please.
Put a vent hole in anything you weld that will be sealed up completely: Put a vent hole in anything you weld that will be sealed up completely or air will heat up and expand and blow away your shielding gas or even blow out at the end of the weld bead. Some machined joints that are sealed on one end will not even allow you to start welding because the fit is so good that the part is air tight before you even weld. Other machined parts where a part is pressed in and bottomed out can give cracking problems because there is no where for the part to shrink. If you have to weld something that has been pressed in and bottomed out, make sure to add more filler metal than average to tacks and the final weld bead. That is to prevent the cracking that happens when you run a concave bead and the metal has nowhere to shrink.
First, practice handling the gun without actually welding. Rest its barrel in one hand, and support that hand on the table. The other hand operates the gun’s trigger. Stand in a comfortable position and move the gun steadily over the work surface. Adjust your posture and gun movement so that they feel natural. Attach the work lead to the workpiece, and hold the gun so the wire meets the weld surface at about a 30-degree angle. Touch the wire very lightly to the surface, squeeze the trigger, and gently pull the gun toward you to make your first test weld. The wire should melt off into the weld puddle at an even rate and make a steady crackling noise as you go. Adjust the welder settings if needed.
Looking for the best Welding Equipment? We recommend Welding Supplies Direct & Associate company TWS Direct Ltd is an online distributor of a wide range of welding supplies, welding equipment and welding machines. We supply Plasma Cutters, MIG, TIG, ARC Welding Machines and support consumables to the UK, Ireland and Europe.
Contact tips can have a significant impact on MIG welding performance since this consumable is responsible for transferring the welding current to the wire as it passes through the bore, creating the arc. The position of the contact tip within the nozzle, referred to as the contact tip recess, is just as important. The correct contact recess position can reduce excessive spatter, porosity, insufficient penetration, and burn-through or warping on thinner materials. While the ideal contact tip recess position varies according to the application, a general rule of thumb is that as the current increases, the recess should also increase.